3M Double Coated Tape 9080HL Tissue Tape
Strong and versatile bonding solution
3M™ Double Coated Tape 9080HL is a white/translucent, general-purpose double-sided tape with a non-woven tissue carrier and high-tack acrylic adhesive. It features excellent initial tack, strong shear resistance, good heat resistance, and reliable bonding to low-surface-energy (LSE) materials (e.g., PE, PP, PVC). Specially designed for high-speed splicing and processes involving heat-setting/oven curing, with easy die-cutting and clean peeling.
Parameter | Details |
Product Number | 9080HL |
Product Type | Double Coated Non-woven (Tissue) Tape |
Carrier/Backing | White non-woven tissue |
Adhesive | High-tack acrylic pressure-sensitive |
Tape Color | White / Translucent |
Total Thickness (without liner) | 0.16 mm (6.3 mil) |
Liner | White polycoated kraft (PCK) paper (3M logo printed) |
Standard Roll Sizes | 1200 mm × 50 m; custom widths (12/19/25/38/50 mm) |
180° Peel Adhesion (Steel, 72h) | 7.5 N/10 mm (ASTM D3330) |
Static Shear Strength | >10,000 minutes (500g, 6.45cm², 22°C, ASTM D3654) |
Long-Term Temperature Resistance | 90–120 °C |
Short-Term Temperature Resistance | Up to 120 °C |
Hot Splicing Resistance | >170 °C (BTM 220 test) |
Liner Release Force | Max. 50 g/in (25.4mm width) |
Shelf Life | 12 months (21°C, 50% RH) |
Key Applications | High-speed splicing (paper/film), bonding LSE plastics (PE/PP/PVC), foam/leather/metal lamination, nameplates, die-cut parts |
Key Features vs. 9448A / 9080A
Higher temperature resistance than 9448A (up to 120°C short-term).
Stronger bonding to LSE materials (PE/PP/PVC) vs. 9448A.
Optimized for splicing & heat processes (oven/heat-setting compatible).
Thicker (0.16mm) than 9448A/9080A (0.15mm) for slightly more conformability.
High shear & clean peel for industrial assembly